Angle TRIGLASS® profiles – fibreglass

ANGLE TRIGLASS ® composite profiles (GRP – FRP – CRP), reinforced with fibreglass and/or carbon, represent one of the pultruded profiles made by Top Glass.

Partially available from stock, depending on the thickness of the matrix employed in their manufacture, our L profiles can be used as components of fibreglass ladders, in frames for the construction of electrical cabins, in wastewater treatment systems and for walking surfaces and frames.

Angle profile

In-stock profiles are in red
Profiles available upon request are in grey
Measurement units: mm

 

The dimensions listed in red are in stock (subject to prior sale), while those in grey , are available upon request and can be custom produced with a variety of reinforcements, resins and colours.

 

SPECIFICATIONS OF IN-STOCK PROFILES

LENGTH IN STOCK: 2.000/6.000 mm

COLORE A STOCK:

  • WHITE FOR ANGLES WITH 2 mm THICKNESS
  • RED FOR ANGLES WITH 3 mm THICKNESS
  • GREY FOR ANGLES WITH 5/8 mm THICKNESS

MATRIX IN STOCK:

  • STANDARD POLYESTER FOR 5/8 mm THICKNESS
  • SELF-EXTINGUISHING POLYESTER IS 213 / UL 94 V0 FOR 2/3 mm THICKNESS
download technical sheet
BaseEightTH.
15152
20203
21141,8
25152
25253
30303
30304
30305
35152
35353
35355
40403
40405
45152
45253
45453
45455
50503
50505
55555
60603
60605
65605
70253
70303
75508
1001008
112453
140603

MEAN PHYSICAL-MECHANICAL PROPERTIES

PROPERTYTEST METHODUNITSTANDARD PROFILES MEAN VALUE
Specific weightASTM D792g/cm31,75 ÷ 1,9
Dielectric strengthASTM D149kV/mm3 ÷ 7
Water absorptionISO 62%0,4
Surface resistivityEN 613401012
Loss factor at 50 Hz (Tg δ)ASTM D7028——–0,20
Thermal class——–CLASSF
Longitudinal thermal expansion coefficientISO 11359-2K-18÷11×10-6
Thermal conductivityEN 12667 / EN 12664W/mK0,3
Longitudinal flexural strengthASTM D790MPa300 ÷ 500
Longitudinal flexural modulusEN 13706GPa22 ÷ 28
Longitudinal tensile strengthASTM D638MPa300 ÷ 500
Longitudinal tensile modulusASTM D638GPa22 ÷ 28
Longitudinal compression strengthASTM D695MPa180 ÷ 300
Longitudinal compression modulusASTM D695GPa16 ÷ 20
Fire reactionUL 94CLASSHB
Shear strengthASTM D2344MPa30

 

NOTE

  • HIGHER MECHANICAL VALUES REFER TO PROFILE WITH THICKNESS OVER 4 mm
  • POSSIBLE UL 94 V0 FIRE REACTION WITH OR WITHOUT HALOGENS
  • POSSIBLE TO HAVE IN ANTISTATIC FORMULATION
  • POSSIBLE USE OF SPECIAL FORMULATION ON THICKNESS OVER 2,5 mm FOR HIGH FIRE REACTION AND NO TOXIC SMOKE
  • VINYLESTER FORMULATION FOR CHEMICAL RESISTANCE APPLICATION AVAILABLE

VALUES REFER TO REINFORCED PROFILES WITH FIBREGLASS IN A POLYESTER MATRIX
Tolerance for mechanical properties refers to longitudinal direction: ± 10%.
The data provided is accurate. However, Top Glass does not assume any liability as to its use.